Treatment method of blast furnace splash

The spatter of the taphole severely reduces the life of the refractory material in the main ditch; it causes iron loss and affects the economic indicators of the blast furnace; due to the spatter, the blast furnace slag iron is not clean, which directly affects the blast furnace condition and causes a greater economic loss. Blast furnace splashing is mainly caused by the gas or water vapor in the blast furnace entering the iron hole through the cracks, causing the iron hole to splash. The processing method is:

1. Make iron out of the nest

That is to say, after the iron hole is drilled, if the splashing is serious, the gun can be blocked immediately, but the mud can not be hit too much, and the hole of the iron hole can be blocked. After a few minutes, the iron is re-tapped, which is what is called “making a nest”. iron. The principle is that the molten iron is pressed out of the iron hole by the pressure in the furnace, and the pressure of the blow-by gas is basically equal to the pressure of the hearth. At this time, the gun is blocked due to the high pressure of the gun piston. The pressure of the blow-by gas, so a small amount of molten iron will be pressed into the gap between the gas and the hole of the iron hole under the action of the pressure, and the gun mud that has been driven into the iron hole is sealed in the gap and solidified, thereby sealing the gap and blocking the gas. effect.

This method is easy to implement, simple to operate, and can effectively inhibit the spattering problem of the iron hole, but it causes repeated consumption of materials in front of the furnace and cannot eliminate the spattering problem of the iron hole.

2. Using special gun mud

As a refractory material that blocks the tap hole and directly contacts the splashed iron flow, gun mud plays a vital role in stabilizing the tapping of the blast furnace and restraining the tap hole from splashing. The selection of high-quality gun mud with good physical and chemical properties (high body density, low porosity, good corrosion resistance and erosion resistance at room temperature and high temperature, etc.) can effectively inhibit the spatter of the iron mouth and improve the state of the iron mouth.

However, high-quality gun clay is relatively expensive, and long-term use will inevitably increase the cost of pig iron, and the use of high-quality gun clay cannot solve the problem of iron spatter from the root.

Treatment method of blast furnace splash

3. Refractory material press-in

The grouting method is used in the iron port and tuyere area to press in the fluid refractory material. When the fluid refractory material is solidified, it will block the gas channel stringing into the iron port, so as to solve the problem of iron port splashing. When the blast furnace is closed, open a hole in the furnace skin and weld the valve; when the blast furnace is produced, the valve is regularly opened for a certain period of time to allow the gas in the furnace to rush out to form a through hole; when the blast furnace is closed again, the slurry is fully compressed Press into the pore to close the gas passage and solve the problem of spattering at the iron port; to choose the appropriate equipment pressure, if the pressure is too large, it will cause damage to the cooling wall, while the pressure is too small to achieve the effect.